reinforced nylon PA engineering plastic granules

reinforced nylon PA engineering plastic granules
reinforced 50%
engineering plastic granules
high temper

 

Performance	Test condition	Testing standard	Units	B2HG8P
Mechanical property
Tensile strength	5mm/min	ISO527-1/2	Mpa	183
Elongation at break	5mm/min 50mm/min	ISO527-1/2	%	4
Bending modulus	2mm/min	ISO178	Mpa	8500
Bending strength	2mm/min	ISO178	Mpa	293
Charpy notched impact strength	23°C	ISO179/leA	KJ/m2	20
Charpy unnotched impact strength	23°C	ISO179/leA	KJ/m2	90
Thermal
Melting	DSC.10K/min	ISO3146	°C	225
Heat distortion temp. A	1.8Mpa	ISO75	°C	225
Heat distortion temp. B	0.45Mpa	ISO75	°C	235
Electrical property
Surface resistivity		IEC60093	Ohm	1/0.1
Volume resistivity		IEC60093	Ohm×cm	10/0.1
Anti-arc-track of	TestotutionA	IEC60012	V
Physical property
Density	23°C	ISO1183	g/cm3	0.7
Hygroscopicity	23°C,50%r.h	ISO62	%
Absorbent/water absorption	23°C /saturtion	ISO62	%
Radial shrinkage	flow	ISO294-4	%
Transverse shrinkage	transverse	ISO294-4	%
Flame retardant
Flammability test	1.6/3.0mm			HB
The level of flame-retardant test	1mm thickness	UL94
Material description				PA6+40%GF High strength

the color is nature, but we can supply colorful products match your requirements.