reinforced with GF PA66 modified nylon66 engineering plastic granules
Product Detailed
Wear- resistant
30% GF
reinforced
Performance | Test condition | Testing standard | Units | AZ601 |
Mechanical property | ||||
Tensile modulus | 50mm/min | ISO527-1/2 | Mpa | |
Yield stress | 50mm/min | ISO527-1/2 | Mpa | |
Tensile strength | 50mm/min | ISO527-1/2 | Mpa | 175 |
Elongation at break | 5mm/min 50mm/min | ISO527-1/2 | % | 2.12 |
Bending modulus | 2mm/min | ISO178 | Mpa | 9600 |
Bending strength | 2mm/min | ISO178 | Mpa | 248 |
Charpy notched impact strength | 23°C | ISO179/leA | KJ/m2 | 12.6 |
Charpy unnotched impact strength | 23°C | ISO179/leA | KJ/m2 | 65 |
Thermal | ||||
Melting | DSC.10K/min | ISO3146 | °C | 265 |
Heat distortion temp. A | 1.8Mpa | ISO75 | °C | 250 |
Heat distortion temp. B | 0.45Mpa | ISO75 | °C | 255 |
Electrical property | ||||
Surface resistivity | IEC60093 | Ohm | 1/0.1 | |
Volume resistivity | IEC60093 | Ohm×cm | 10/0.1 | |
Anti-arc-track of | TestotutionA | IEC60012 | V | |
Physical property | ||||
Density | 23°C | ISO1183 | g/cm3 | |
Hygroscopicity | 23°C,50%r.h | ISO62 | % | |
Absorbent/water absorption | 23°C /saturtion | ISO62 | % | 0.9 |
Radial shrinkage | flow | ISO294-4 | % | 0.58 |
Transverse shrinkage | transverse | ISO294-4 | % | 0.25 |
Flame retardant | ||||
Flammability test | 1.6/3.0mm | UL94 | ||
The level of flame-retardant test | 1mm thickness | ISO3795 | mm/min | |
Material description | PA66+30GF wear-resisitant MOS2 |